WM, 5X00IN21 Working With Body Structural Adhesive Pah.071.781.00: Notes
WARNING: This page does not describe the selected car, but rather 10 other vehicles, including the 2021 Porsche 718 Cayman, 2021 Porsche 718 Boxster, 2020 Porsche 718 Cayman, 2020 Porsche 718 Boxster, and 2019 Porsche 718 Cayman. However, it is still accessible from the selected car via links, so may be relevant.
TOOL DESCRIPTION
| Tool denomination | Type | Tool number | Image |
|---|---|---|---|
| hand-cartridge gun | Vehicle-specific workshop equipment | > V.A.G 1628 | |
| pneumatic gun | General workshop equipment | > VAS 6648 | |
| pneumatic cartridge gun | General workshop equipment | > V.A.G 1761/1 |
TECHNICAL VALUE SPECIFICATION
| Location | Description | Type | Basic value | Tolerance 1 | Tolerance 2 |
|---|---|---|---|---|---|
| Minimum processing temperature | PAH.071.781.00 | Minimum temperature | 15°C | ||
| Maximum processing temperature | PAH.071.781.00 | Maximum temperature | 35°C | ||
| Structural bonding | PAH.071.781.00 | Processing time at 15°C | 80 min | ||
| Structural bonding | PAH.071.781.00 | Processing time at 18°C | 75 min | ||
| Structural bonding | PAH.071.781.00 | Processing time at 20°C | 65 min | ||
| Structural bonding | PAH.071.781.00 | Processing time at 23°C | 60 min | ||
| Structural bonding | PAH.071.781.00 | Processing time at 25°C | 50 min | ||
| Structural bonding | PAH.071.781.00 | Processing time at 30°C | 40 min | ||
| Structural bonding | PAH.071.781.00 | Processing time at 35°C | 30 min | ||
| Applying adhesive | Spread out evenly | Application depth | 0.5 mm | ||
| Maximum layer thickness | Layer thickness | 1 mm | |||
| Minimum hardening temperature | PAH.071.781.00 | Minimum temperature | 18°C | ||
| Maximum hardening temperature | PAH.071.781.00 | Maximum temperature | 80°C | ||
| Assembly strength | PAH.071.781.00 | Hardening time at 23°C | 12 h | ||
| Assembly strength | PAH.071.781.00 | Hardening time at 60°C | 60 min | ||
| Endurance strength | PAH.071.781.00 | Standing time at 18°C | 96 h |