| Minimum processing temperature |
Betamate 2096 |
Minimum temperature |
15°C |
|
|
| Maximum processing temperature |
Betamate 2096 |
Maximum temperature |
35°C |
|
|
| Optimal processing temperature |
Betamate 2096 |
Minimum temperature |
18°C |
|
|
| Optimal processing temperature |
Betamate 2096 |
Maximum temperature |
23°C |
|
|
| Structural bonding |
Betamate 2096 |
Processing time at 15 °C |
75 min |
|
|
| Structural bonding |
Betamate 2096 |
Processing time at 18 °C |
70 min |
|
|
| Structural bonding |
Betamate 2096 |
Processing time at 20 °C |
65 min |
|
|
| Structural bonding |
Betamate 2096 |
Processing time at 23 °C |
60 min |
|
|
| Structural bonding |
Betamate 2096 |
Processing time at 25 °C |
55 min |
|
|
| Structural bonding |
Betamate 2096 |
Processing time at 30 °C |
45 min |
|
|
| Structural bonding |
Betamate 2096 |
Processing time at 35 °C |
35 min |
|
|
| Length of adhesive bead |
|
Length |
10 cm |
|
|
| Applying adhesive |
Spread out evenly |
Application depth |
0.5 mm |
|
|
| Bead of adhesive |
|
Application depth |
3 mm |
|
|
| Maximum layer thickness |
|
Layer thickness |
1 mm |
|
|
| Minimum hardening temperature |
Betamate 2096 |
Minimum temperature |
18°C |
|
|
| Maximum hardening temperature |
Betamate 2096 |
Maximum temperature |
80°C |
|
|
| Assembly strength |
Betamate 2096 |
Hardening time at 18 °C |
12 h |
|
|
| Assembly strength |
Betamate 2096 |
Hardening time at 60 °C |
35 min |
|
|
| Endurance strength |
Betamate 2096 |
Standing time at 18 ° C |
96 h |
|
|
| Primer |
|
Flash-off time |
5 min |
|
|