Machining/Treating Magnesium Components Information - Ah60.00-P-0023-01R

WARNING: This page does not describe the selected car, but rather 12 other vehicles, including the 2023 Mercedes-Benz CLA45 AMG, 2023 Mercedes-Benz CLA35 AMG, 2023 Mercedes-Benz CLA250, 2022 Mercedes-Benz CLA45 AMG, and 2022 Mercedes-Benz CLA35 AMG. However, it is still accessible from the selected car via links, so may be relevant.

Model all (CAR)

General:

Magnesium has the property of forming a compound with oxygen extremely quickly. Nevertheless it is corrosion-resistant when exposed to air, because it forms a tight, continuous thin oxide skin which protects the metal beneath from further oxidation.

If magnesium ignites, then it burns at approx. > 500°C with a blinding white light and strong heat development

(approx. 2400°C).

Magnesium dust combusts and explodes just as easily as aluminum dust.

For additional information see Accident Prevention Regulations or the regulations of the trade association.

Machining/treating magnesium:

Machining/treating magnesium components by means of an open flame (welding, cutting, soldering, heating, etc.) or by spark-creating grinding is prohibited.
Any components that suffer structural damage must be replaced completely.

Corrosion protection:

Faulty coatings and points affected by corrosion should never be repaired for corrosion reasons.
Repair over large surfaces should not be performed for reasons of corrosion.
To prevent contact corrosion on the threaded connections of the components
(e.g. internal door parts); the contact surfaces and screw shanks must be coated with paint or the screws must be replaced after dismantling.

Do not use zinc dust paint!

Plastic bushings and disks installed as standard must not be removed and damaged parts must be replaced.
Due to extremely severe contact corrosion, damaged threads in the magnesium pressure castings may only be repaired with the MB-approved Helicoil thread inserts made of aluminum.